添加时间2018-10-03  信息来源http://www.amsaquaticservice.com/  作者苏州希普能塑料
Kynar Flex 2950-05
Kynar Flex® 2950-05
聚偏二氟乙烯
Arkema Technical Polymers
 
产品说明:
Kynar Flex® resins are fluorinated thermoplastic copolymers.
 
Kynar Flex® 2950-05 resin is a pelletized, semi-crystalline VF2 based copolymer. It has been designed for wire and cable applications requiring high flexibility and improved resistance to impact.The low molecular weight allows extrusion conditions that reduce jacket shrink back over fiber optic constructions.
 
Additional characteristics:
Excellent thermal stability
Excellent abrasion resistance
Excellent chemical resistance
Impervious to UV degradation
High Limiting Oxygen Index
Extremely low smoke emission characteristics
 
Meets UL910 requirements
 
材料特点High Flexibility半结晶低分子量低烟度共聚物抗紫外线性能良好良好抗撞击性良好耐磨损性耐化学热稳定
材料应用电线电缆应用
外观形式粒子
供货地区北美洲非洲和中东拉丁美洲分ޡ亚太地区
加工方法挤出
中国代理苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 额定值 单位制 测试方法
密度 1.77 g/cm³ ISO 1183
熔融体积流量MVR(232/3.8 kg) 11.5 cm³/10min ISO 1133
吸水率(饱和,23) 0.030 % ISO 62
机械性能 额定值 单位制 测试方法
拉伸模量 387 MPa ISO 527-2
拉伸应力(屈服) 17.0 MPa ISO 527-2
拉伸应变(屈服) 18 % ISO 527-2
标称拉伸断裂应变 > 50 % ISO 527-2
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23) 无断裂   ISO 179/1eA
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 57.0 ISO 75-2/B
1.8 MPa,未退火 43.0 ISO 75-2/A
玻璃转化温度1 -34.0 ISO 11357-2
熔融温度1 134 ISO 11357-3
电气性能 额定值 单位制 测试方法
体积电阻率 2.0E+14 ohms·cm IEC 60093
介电强度 1.4 kV/mm IEC 60243-1
相对电容率(100 Hz) 7.05   IEC 60250
耗散因数(100 Hz) 0.12   IEC 60250
可燃性 额定值 单位制 测试方法
可燃性燃(1.5 mm) V-0   IEC 60695-11-10,-20
V-0  
极限氧指数 95 % ISO 4589-2
备注
1 10/min